Tungsten Alloy Swaging Rod for CNC Toolings, Anti-Seismic Mill Holder

Introduction of Tungsten Alloy swaged rod

The normal tungsten alloy rod after swaging, ultimate tensile strength and hardness would be increased greatly. The ultimate tensile strength of general tungsten alloy rod is 920 MPa, hardness is 25HRC. However, after swaging, the ultimate tensile strength can reach 1200 MPa, hardness is 35HRC. We could even control at 1400 MPa, 40HRC. This type of rod is one of our main products. Usually the composition of this kind of products is 92%WNiFe.

1. Dimension: Diameter≥8.3mm, Length≤700mm

2. Density: 17.0-18.10 g/cm3
3. Composition: W content: 92~95%, W-Ni-Fe
4. Surface: swaged state

 

Tungsten Alloy Military Swaging Rod Main Properties:

* High density 
* High melting point 
* Small volume 
* Excellent hardness 
* Superior wearing resistance 
* High ultimate tensile strength 
* High ductility 
* High temperature resistance 
* Low vapor pressure

 

Appliance of tungsten heavy alloy swaged rod

Tungsten alloy swaging rod can be use in machining, CNC toolings, anti-seismic mill holder etc.

 

GradeState Density
(g/cc)
UST Elongation
(%)
Hardness
(HRC)
Impact toughness
(MJ/m2)
Yield strength
(MPa)
W263Swaging17.25±0.15≥1450≥8≥35≥0.3≥1350
W262Swaging17.50±0.15≥1450≥5≥35≥0.3≥1350
W261Swaging17.60±0.15≥1050≥6≥35≥0.3≥900
W253Swaging17.40±0.15≥1450≥8≥35≥0.3≥1375
W243Swaging17.60±0.15≥1450≥7≥35≥0.3≥1375
W232Swaging18.10±0.15≥1400≥6≥37≥0.1≥1350
W231Swaging18.30±0.15≥1050≥3≥37≥0.1≥800
W221Swaging18.50±0.15≥1350≥2≥37≥0.07≥1250